POM EB-10日本宝理--Eb-10 is a Polyoxymethylene (POM) copolymer product,. It can be processed by injection molding and is available in North America, Europe or Asia Pacific.
Features include:
Flame retardant / rated flame
Conductivity
Antistatic
carbon black
Eb-10 physical property table
essential information
Yellow card number
E45034-235718
additive
Antistatic Carbon Black (10%)
characteristic
Conductive antistatic property
UL file number
E45034
form
particle
Processing method
injection molding
Part identification code (ISO 11469)
>POM-CD10
Physical performance rating unit system test method
Density: 1.43 g / cm? ISO 1183
Melt flow rate (melt flow rate) (190 ° C / 2.16 kg) 1.5 g / 10 min ISO 1133
MVR (190 ° C / 2.16 kg) 1.20 cm3 / 10min ISO 1133
Water absorption (23 ° C, 24 hr) 0.80% ISO 62
Hardness rating unit system test method
Rockwell hardness (M scale) 95 ISO 2039-2
Mechanical properties rating unit system test method
Tensile modulus 3300 MPa ISO 527-2
Tensile stress 55.0 MPa ISO 527-2
Tensile strain (fracture) 3.0% ISO 527-2
ISO 178 MPa bending modulus
Bending stress: 95.0 MPa ISO 178
Friction coefficient JIS k7218
Dynamic 1 0.36 JIS K7218
And steel - Dynamic 2 0.52 JIS k7218
Wear factor JIS k7218
0.98 MPa, 0.30 m/sec 3 < 1.0 10^-8 mm³/N·m JIS K7218
0.060 MPa, 0.15 m/sec 4 57 10^-8 mm³/N·m JIS K7218
0.98 MPa, 0.30 m/sec 5 60 10^-8 mm³/N·m JIS K7218
0.060 MPa, 0.15 m/sec 6 200 10^-8 mm³/N·m JIS K7218
Impact performance rating unit system test method
Notched impact strength of simply supported beam: 1.8 kJ / M? ISO 179 / 1ea
Thermal performance rating unit test method
Hot deformation temperature (1.8 MPa, UN annealed) 95.0 ° C ISO 75-2 / A
Linear coefficient of thermal expansion internal method
Flow: 23 to 55 ° C 1.1e-4 cm / cm / ° C internal method
Transverse: 23 to 55 ° C 1.1e-4 cm / cm / ° C internal method
Electrical performance rating unit system test method
Internal method of surface resistivity 2.0e + 2 ohms
Internal method of volume resistivity 50 ohms · cm
Flammability rating unit system test method
UL flame retardant grade HB UL 94
Supplementary information - Rating
Color Number CD3501
Injection rating unit system
Drying temperature: 80.0 to 90.0 ° C
Drying time: 3.0 to 4.0 HR
Processing (melt) temperature 190 to 210 ° C
Mold temperature: 60.0 to 80.0 ° C
Injection pressure: 49.0 to 98.0 MPa
Screw speed: 100 to 150 rpm