PMMA 8NDF22德固赛---Superior light diffusion and tran***ittance is obtained by incorporation of spherical, high MW polymer beads of a different refractive index into the acrylic matrix. Used in lighting, optoelectronics, displays, monitor covers, and projection screens.
热性能 额定值 (公制) 额定值 (英制) 测试方法
线性热膨胀系数 72.0 µm/m-°C
@Temperature 0.000 - 100 °C
40.0 µin/in-°F
@Temperature 32.0 - 212 °F
ASTM D696
载荷下热变形温度(1.8 MPa) 105 °C
@Thickness 6.35 mm
221 °F
@Thickness 0.250 in
Annealed; ASTM D648
维卡软化温度 119 °C 246 °F ASTM D1525
光学性能 额定值 (公制) 额定值 (英制) 测试方法
折射率 1.50 1.50 ASTM D542
雾度 94 % 94 % ASTM D1003
Yellow Index <= 4.5 % <= 4.5 % ASTM D1925
Tran***ission, Visible 88 % 88 % ASTM D1003
加工性能 额定值 (公制) 额定值 (英制) 测试方法
料筒中部温度 240 - 250 °C 464 - 482 °F Cylinder Temp
加工(熔体)温度 240 - 250 °C 464 - 482 °F
模具温度 37.8 - 79.4 °C 100 - 175 °F
干燥温度 79.4 °C 175 °F
干燥时间 3 - 4 hour 3 - 4 hour