PA6 1013B日本宇部---UBE Nylon 1013B是一种聚酰胺6（尼龙6）产品,。 它可以通过***成型进行加工,在北美洲有供货。
特性包括:
- 阻燃/额定火焰
- 耐***
- 坚硬
- 耐冲击
- 耐磨
Unit system test method for physical properties after drying and adjustment
Specific gravity: 1.14 -- g / cm 3 ASTM D792
Shrinkage - flow 1.4 to 1.5 --% ASTM D955
Water Absorption ASTM D570
24 hr 1.8 -- % ASTM D570
Saturated 11 --% ASTM D570
Unit system test method for hardness, drying and adjustment
Rockwell hardness ASTM d785
Grade m 85.55 ASTM d785
Grade R 120.85 ASTM d785
Mechanical properties - unit system test method after drying and adjustment
Tensile strength ASTM D638
Yield: 73.5 39.2 MPa ASTM D638
Fracture: 63.7 -- MPa ASTM D638
Elongation ASTM D638
Yield 8.0 --% ASTM D638
Fracture 170 200% ASTM D638
Bending modulus: 2550 735 MPa ASTM D790
Bending strength (yield) 108 39.2 MPa ASTM D790
Compressive strength: 19.6 ~ 9.80 MPa ASTM d695
Shear strength 63.7 58.8 MPa ASTM d732
Impact performance - unit system test method after drying and adjustment
Notched impact strength of cantilever beam ASTM D256
-30°C 39 -- J/m ASTM D256
23°C 59 490 J/m ASTM D256
Unit system test methods for thermal performance, drying and conditioning
Hot deformation temperature under load ASTM D648
0.45 MPa, UN annealed at 175 - - C ASTM D648
1.8 MPa, UN annealed at 75.0-- ° C ASTM D648
The melting temperature is 215 to 225-- ° C
Linear coefficient of thermal expansion - flow 8.0e-5 -- cm / cm / ° C ASTM d696
RTI Elec (0.794 mm) 65.0 -- °C UL 746
RTI Imp (0.794 mm) 65.0 -- °C UL 746
RTI (0.794 mm) 65.0 -- °C UL 746