PA6 1010C2荷兰D***---1010c2 is a polyamide 6 (nylon 6) material,. The product is available in Asia Pacific region, and the processing method is injection molding.
The main characteristics of 1010c2 are as follows:
Flame retardant / rated flame
Good processing performance
Unit system test method for physical properties after drying and adjustment
Density: 1.13 -- g / cm 3 ISO 1183
Shrinkage: ISO 294-4
Vertical flow direction 1.1 --% ISO 294-4
Flow direction 1.0 --% ISO 294-4
Water absorption (balanced, 23 ° C, 50% RH) 2.8 --% ISO 62
Viscosity 118 -- cm 3 / g ISO 307
Mechanical properties - unit system test method after drying and adjustment
Tensile modulus 3400 1700 MPa ISO 527-2
Tensile stress (yield) 87.0 54.0 MPa ISO 527-2
Tensile strain (yield) 4.2 21% ISO 527-2
Nominal tensile breaking strain 18 > 50% ISO 527-2
Bending modulus 2800 1000 MPa ISO 178
Bending stress 112 49.0 MPa ISO 178
Impact performance - unit system test method after drying and adjustment
Notched impact strength of simply supported beam (23 ° C) 4.4 26 kJ / M? ISO 179
Notchless impact strength of simply supported beam (23 ° C) no fracture ISO 179
Unit system test methods for thermal performance, drying and conditioning
Hot deformation temperature
0.45 MPa, UN annealed 180 - - C ISO 75-2 / b
1.8 MPa, UN annealed at 65.0-- ° C ISO 75-2 / A
Melting temperature: 1 220 - - C ISO 11357-3
Linear coefficient of thermal expansion ISO 11359-2
Flow 7.0e-5 -- cm / cm / ° C ISO 11359-2
Transverse 8.0e-5 -- cm / cm / ° C ISO 11359-2
Unit system test method for electrical performance after drying and adjustment
Surface resistivity - 2.0e + 14 ohms IEC 60093
Volume resistivity > 1.0e + 15 -- ohms · cm IEC 60093
Dielectric strength 27 -- kV / mm IEC 60243-1
Relative permittivity IEC 60250
100 Hz 4.00 -- IEC 60250
1 MHz 4.00 -- IEC 60250
Dissipation factor IEC 60250
100 Hz 0.011 -- IEC 60250
1 MHz 0.023 -- IEC 60250
Leakage tracking index 600 -- V IEC 60112
Unit system test method for flammability, drying and adjustment
Flammability class (0.800 mm) V-2 -- IEC 60695-11-10, - 20
Injection drying unit system
Drying temperature: 80.0 ° C
Drying time is from 4.0 to 8.0 hr
Barrel rear temperature 230 to 235 ° C
The temperature in the middle of the barrel is 235 to 250 ° C
Barrel front temperature 240 to 260 ° C
Nozzle temperature 240 to 270 ° C
Processing (melt) temperature 240 to 275 ° C
Mold temperature: 50.0 to 80.0 ° C
The injection speed was medium to high
Back pressure: 3.00 to 10.0 MPa
Screw compression ratio: 2.5:1.0