美瑞化学聚脂型产品物性表
——聚脂型材料物性表
|
性能 Properties
|
ASTM
|
单位
|
E270
|
E180
|
E185
|
E190
|
E195
|
E155D
|
E165D
|
E175D
|
|
密度 Density
|
D0792
|
g/cm3
|
1.18
|
1.19
|
1.19
|
1.19
|
1.20
|
1.21
|
1.21
|
1.22
|
|
硬度 Hardness
|
D2240
|
Shore A/D
|
72A
|
82A
|
86A
|
92A
|
95A
|
97A
|
65D
|
73D
|
|
抗张强度
Tensile Strength
|
D412
|
Mpa
|
20
|
28
|
32
|
34
|
38
|
38
|
40
|
41
|
|
100%模量
100%Modulus
|
D412
|
Mpa
|
3
|
3
|
6
|
9
|
13
|
15
|
20
|
30
|
|
300%模量
300%Modulu
|
D412
|
Mpa
|
5
|
9
|
14
|
18
|
25
|
28
|
35
|
35
|
|
断裂伸长率
Elongation at Break
|
D412
|
%
|
610
|
550
|
500
|
420
|
360
|
340
|
300
|
250
|
|
撕裂强度
Tear Strength
|
D624
|
KN/M
|
60
|
90
|
100
|
120
|
140
|
170
|
210
|
260
|
|
Taber磨耗
Taber Abrasion Loss
|
D1044
|
mg
|
80
|
15
|
15
|
15
|
20
|
35
|
35
|
35
|
|
玻璃化转变温度
Tg(DSC,10’C/min)
|
D3417
|
‘c
|
-42
|
-40
|
-38
|
-34
|
-30
|
-27
|
-25
|
-20
|
|
压缩变型
Compression Set
|
D395
|
%
|
25
|
25
|
25
|
25
|
30
|
30
|
-
|
-
|
|
D395
|
%
|
48
|
48
|
45
|
45
|
50
|
55
|
-
|
-
|
|
|
成型温度
|
‘C
|
170-200
|
170-200
|
170-205
|
170-210
|
170-215
|
170-215
|
180-220
|
185-220
|
|