| 规格级别 | 薄膜 | 外观颜色 | |
| 该料用途 | 加工薄膜 | ||
| 备注说明 | 特性：良好的加工性 | ||
| 加工条件 |
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.922 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 5 | g/10min | |||
| 物理性能 | 光泽度 | 60℃ | ASTM D-2457 | 10 | g/µm | |
| 混浊 | ASTM D-1003 | 7 | % | |||
| 机械性能 | 极限伸长率 | MD | ASTM D-882 | 250 | % | |
| TD | ASTM D-882 | 440 | % | |||
| 1%割线模量 | MD | ASTM D-882 | 220 | MPa | ||
| TD | ASTM D-882 | 270 | MPa | |||
| Dart drop impact | ASTM D-1709 | 2.5 | g/µm | |||
| Elmendort断裂强度 | MD | ASTM D-1922 | 9.5 | g/µm | ||
| TD | ASTM D-1922 | 4 | g/µm | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 19 | MPa | ||
| TD | ASTM D-882 | 25 | MPa | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 93 | ℃ | ||