无缝管-聊城鲁发钢管厂

· 可供规格size： 热挤压管hot extrusion tube：外径OD：48~325mm；壁厚WT：4~40mm；

冷加工管cold rolling tube：外径OD：5.8~273mm；壁厚WT：0.3~35mm。

· 订货标准standard：ASTM A312/A***E SB677，企业标准，技术协议

· 交货状态condition：热挤压hot extrusion；冷加工cold rolling；热处理heat treatment

主要钢种（牌号）的化学成分和性能chemical composition and performance of main steel grade(trademark)

ASTM UNS牌号

grade化学成分chemical compositionCSiMnPSNiCrMoCuNFeWT%N08904904L≤0.020≤1.00≤2.00≤0.045≤0.03523.0-28.019.0-23.04.0-5.01.0-2.0-余N08367AL-6XN≤0.030≤1.00≤2.00≤0.040≤0.04023.5-25.020.0-22.06.0-7.0≤0.750.18-0.25余S31254254***o≤0.020≤0.80≤1.00≤0.030≤0.01017.5-18.519.5-20.56.0-6.50.5-1.00.18-0.22余S32654654***o≤0.020≤0.302.0-4.0≤0.005≤0.00521.0-23.024.0-25.07.0-8.00.3-0.60.45-0.55余

室温力学性能room-temperature mechanical property

ASTM UNS热处理温度

Temperature抗拉强度

Rm， min，MPa屈服强度

Rp0.2%，min，MPa伸长率

A50，无缝管，min，%N08904≥1100℃49022035N08367≥1100℃69031030S31254≥1150℃67531035S32654≥1150℃75043035

晶间腐蚀性能intergranular corrosion resistance

按ASTM G28A法（***铁-***法）测定的腐蚀速率

Intergranular corrosion resistance according to ASTM G28(ferric sulfate- sulfuric acid method)

钢种

grade状态

condition时间

(h)腐蚀速率

mm/a腐蚀深度

(μm)N08904固溶solution1200.35≤50

按ASTM 262C法65%***法测定的腐蚀速率

Intergranular corrosion resistance according to ASTM 262(65% HNO3)

钢种

grade状态

condition腐蚀速率corrosion rate(mm/a)平均腐蚀深度

corrosion rate(mm/a)一二三四五时间/48h时间/48h时间/48h时间/48h时间/48hN08904固溶solution0.190.180.290.480.670.36

对现在的人们来说，很是熟悉。因为它在各个领域都起着举足轻重的作用。我们中国的在1953年10月27日，根无缝钢管试轧成功，这也是1953年我国重工业发展中的巨大事件。或许，无缝钢管并不是什么高科技产品，但正是因为有了它才有了我们的工业的发展。

作为输送管运输着油、气体、水源等各个流体。它就像我们***的血管一样，为我们的祖国大地不断的运输和分配着各个能源的合理利用。正是因为有了无缝钢管的高质量高品质的保障，我们的工业才能安心的不断发展，我们的生活也能够有序的进行。

当然，不但在生活工业中起着重要作用，在工业中也是重要的生产材料。比如一些火炮的身管，舰艇动力装置的冷却管，潜艇的发射管等，都被认为。它的特点是：产量相对很低，但是技术含量和造价都比较高，是高品级无缝管的主要代表。

也正是有了的奠定才有了***的强盛，我们才能够真正做到有底气，能够做到国富民强。

***用无缝管

2017/2/15 15:39:44***用无缝管

Seamless pipe in nuclear power

· 用途：用于各种核反应堆的蒸汽发生器、燃料组件、堆内构件、驱动机构、换热器等一、二、三级用管和输送管道

· Usage：applied for pipe and transfer piping of all kinds of vapour generator， feul subassembly， in-pipe part and actuating mechani*** etc， in nuclear reactor.

· 订货标准Order norm：GB13296;GB/T14976;RCCM M4105;NB/T20008.7-2011;A***E SB163;agreement protocol etc

· 可供规格Offer specification：外径OD：8~325mm；壁厚WT：0.5~40mm

主要钢种（牌号）的化学成分和性能chemical composition and performance of main steel grade(trademark)

牌号trademark

原牌号（新牌号）化学成分chemical compositionNiCrFeMnCSiSPAlTiCu其它

othersWT%0Cr18Ni9

(06Cr19Ni10)8.0-

11.017.0-

19.0余bal≤2.0≤0.07≤1.00≤0.030≤0.035----00Cr19Ni10

(022Cr19Ni10)8.0-

12.018.0-

20.0余bal≤2.0≤0.030≤1.00≤0.030≤0.035----0Cr17Ni12Mo2

(06Cr17Ni12Mo2)11.0-

14.016.0-

18.5余bal≤2.0≤0.08≤1.00≤0.030≤0.035----00Cr17Ni14Mo2

(022Cr17Ni12Mo2)12.0-

15.016.0-

18.0余bal≤2.0≤0.03≤1.00≤0.030≤0.035----00Cr25Ni35AlTi34.0-

37.024.0-

26.5余bal0.5-

1.5≤0.0300.30-

0.70≤0.015≤0.0150.15- 0.450.15-

0.60≤0.50Co≤0.05

N≤0.03UNS N0880030.0-

35.019.0-

23.0≥39.5≤1.5≤0.10≤1.00≤0.015-0.15- 0.600.15-

0.60≤0.75-UNS N06600≥72.014.0-

17.06.0-

10.0≤1.0≤0.15≤0.50≤0.015---≤0.5-690

(NC30Fe)≥58.028.0-

31.08.0-

11.0≤0.50.01-

0.03≤0.50≤0.010≤0.015≤0.50≤0.50≤0.50Co≤0.018

Nb≤0.10

B≤0.003

N≤0.05690

(NS3105)≥58.028.0-

31.08.0-

11.0≤0.50.010-

0.03≤0.50≤0.010≤0.015≤0.50≤0.05≤0.05Nb≤0.10

B≤0.003

Co≤0.018

N≤0.05690(UNS NO6690)

A***E SB163及补充技术要求

A***E SB163 and additional technical requirements≥58.028.5-

31.09.0-

11.0≤0.50.015-

0.02≤0.50≤0.010≤0.015≤0.40≤0.35≤0.05Nb≤0.10

B≤0.002

Co≤0.016

N≤0.05

Mo≤0.2

· ASTM SB163 and additional technical requirements

· 690(NC30Fe/UNS N06690/NS3105)***力学性能及尺寸表面要求

技术指导

Standard690(NC30Fe)

RCCM M4105690(NS3105)

NB/T 20008.7-2001690(UNS NO6690)

A***E SB163及补充技术要求

A***E SB163 and additional technical requirements晶粒度

Grain size5-95-9，级差3级细于等于5级，级差小于2级

Less than ASTM5， not exceed two ASTM units室温拉伸

Room temperature tensileRm MPa≥630≥630gt;585Rp0.2 MPa275-375275-375275-380A%≥30≥30≥30350℃拉伸

350℃ tensileRm MPa≥533≥533≥550Rp0.2 MPa≥215≥215gt;215硬度 Hardness≤92≤92-扩口 flare-60°30%60°30%尺寸公差

Dimension tolerance外径OD mm19.05 /-0.0519.05 /-0.0517.48 /-0.05壁厚WT mm1.09 /-0.101.09 /-0.101.01 /-0.09长度L m19-2519-2519-29U形管椭圆度

U-bend tube ovality1-3排lt;5%1-3排≤5%1-5rowlt;2.8%4-6排lt;4%4-6排≤4%6-15rowlt;2.6%7-53排lt;3%7-53排≤3%16-164rowlt;1.6%内涡流性噪比

Noise levelgt;7单点single point≥7单点single point≥20水压试验

Hydrostatic14.7MPax10秒B级水

Demineralized water grade B14.7MPax10秒B级水

Demineralized water grade B21.42MPa≥5秒 ***水

Demineralized water grade A表面粗糙度

Surface roughness内Ralt;0.8、外Ralt;1.2

Inner surface Ralt;0.8

Outer surface Ralt;1.2内Ra≤0.8、外Ra≤1.2

Inner surface Ra≤0.8

Outer surface Ra≤1.2内Ralt;0.5、外Ralt;1.0

Inner surface Ralt;0.5

Outer surface Ralt;1.0晶间腐蚀

Intergranular corrosion--≤20mdd