PC 915AU 抗紫外线
|
MECHANICAL
|
Value | Unit | Standard |
|
Tensile Stress, yld, Type I, 50 mm/min
|
670
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
670
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
100
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
24400
|
kgf/cm²
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
960
|
kgf/cm²
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
24400
|
kgf/cm²
|
ASTM D 790
|
|
Tensile Stress, yield, 50 mm/min
|
66
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
66
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
100
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2400
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
98
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2400
|
MPa
|
ISO 178
|
|
IMPACT
|
Value | Unit | Standard |
|
Izod Impact, notched, 23°C
|
66
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
11
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
611
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m²
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
NB
|
kJ/m²
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*3 +23°C
|
65
|
kJ/m²
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*3 -30°C
|
11
|
kJ/m²
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
65
|
kJ/m²
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
12
|
kJ/m²
|
ISO 179/1eA
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m²
|
ISO 179/1eU
|
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m²
|
ISO 179/1eU
|
|
THERMAL
|
Value | Unit | Standard |
|
Vicat Softening Temp, Rate B/50
|
140
|
°C
|
ASTM D 1525
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
125
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
7.E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate B/50
|
140
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
141
|
°C
|
ISO 306
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
123
|
°C
|
ISO 75/Ae
|
|
PHYSICAL
|
Value | Unit | Standard |
|
Specific Gravity
|
1.2
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
23
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.2
|
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.35
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
21
|
cm³/10 min
|
ISO 1133
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard |
|
UL Recognized, 94V-2 Flame Class Rating (3)
|
1.5
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
3
|
mm
|
UL 94
|
|
Source GMD, last updated:2008/09/30
|
|
Processing
|
| Parameter | ||
|
Injection Molding
|
Value | Unit |
|
Drying Temperature
|
120
|
°C
|
|
Drying Time
|
2 - 4
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
280 - 310
|
°C
|
|
Nozzle Temperature
|
270 - 290
|
°C
|
|
Front - Zone 3 Temperature
|
280 - 310
|
°C
|
|
Middle - Zone 2 Temperature
|
270 - 290
|
°C
|
|
Rear - Zone 1 Temperature
|
260 - 280
|
°C
|
|
Hopper Temperature
|
60 - 80
|
°C
|
|
Mold Temperature
|
80 - 110
|
°C
|