ABS/100-X01/日本东丽
原料描述部分
|
规格级别 |
注塑, 挤出 |
|
备注说明 |
超高抗冲击性，颗粒料 |
原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
|
物理性能 |
吸水率 |
24hr,23℃ |
ASTM D-570 |
0.30 |
% |
|
熔体流动速率 |
220℃/10.0kg |
ISO 1133 |
15 |
g/10min |
|
|
比重 |
|
ASTM D-792 |
1.04 |
g/cm3 |
|
|
ISO 1183 |
|||||
|
模具收缩率 |
流动 |
ASTM D-955 |
0.4-0.6 |
% |
|
|
机械性能 |
拉伸模量 |
|
ISO 527-2/1 |
2100 |
MPa |
|
抗张屈服强度 |
23℃ |
ASTM D-638 |
41.0 |
MPa |
|
|
|
ISO 527-2/50 |
44.0 |
MPa |
||
|
断裂伸长率 |
23℃ |
ASTM D-638 |
40 |
% |
|
|
|
ISO 527-2/50 |
10 |
|||
|
弯曲模量 |
23℃ |
ASTM D-790 |
1960 |
MPa |
|
|
弯曲屈服强度 |
|
ASTM D-790 |
63.0 |
MPa |
|
|
23℃ |
ISO 178 |
||||
|
简支梁缺口冲击强度 |
23℃ |
ISO 179/1eA |
26 |
KJ/m2 |
|
|
悬壁梁缺口冲击强度 |
-30℃,3.20mm |
ASTM D-256 |
157 |
J/m |
|
|
-30℃,12.7mm |
137 |
||||
|
0℃,3.20mm |
226 |
||||
|
℃,12.7mm |
196 |
||||
|
23℃,3.20mm |
314 |
||||
|
23℃,12.7mm |
294 |
||||
|
洛氏硬度 |
|
ASTM D-785 |
118 |
R-scale |
|
|
热性能 |
热变形温度 |
1.80MPa，未退火，6.40mm |
ASTM D-648 |
85.0 |
℃ |
|
1.80MPa，未退火，12.7mm |
91.0 |
||||
|
1.80MPa，未退火 |
ISO 75-2/A |
78.0 |
|||
|
阻燃等级 |
|
UL94 |
HB |
|
|
|
线形膨胀系数 |
流动 |
ASTM D-696 |
0.000076 |
cm/cm/℃ |
|
|
导热系数 |
|
ASTM C-177 |
0.15 |
W/m/K |
|
|
电气性能 |
表面电阻率 |
|
ASTM D-257 |
1.0E+16 |
ohms |
|
体积电阻率 |
23℃ |
ASTM D-257 |
1.0E+16 |
||
|
介电强度 |
|
ASTM D-149 |
24 |
KV/mm |
|
|
介电常数 |
1KHz |
ASTM D-150 |
3.10 |
|
|
|
耗散因数 |
1KHz |
ASTM D-150 |
0.0065 |
|
|