PA6(聚已内酰胺#尼龙6)/CM1016G-30/日本东丽
原料描述部分
|
规格级别 |
玻纤增强 |
|
备注说明 |
玻璃纤维增强 30% |
原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
|
物理性能 |
填充含量 |
|
|
30 |
Wt% |
|
比重 |
|
ASTM D-792 |
1.36 |
g/cm3 |
|
|
吸水率 |
23℃,24hrs |
ASTM D-570 |
1.1 |
% |
|
|
23℃,水中 |
ASTM D-570 |
6.4 |
% |
||
|
洛氏硬度 |
23℃ |
ASTM D-785 |
120/93 |
R/M |
|
|
机械性能 |
拉伸屈服强度 |
-40℃ |
ASTM D-638 |
250 |
MPa |
|
23℃ |
ASTM D-638 |
185 |
MPa |
||
|
80℃ |
ASTM D-638 |
100 |
MPa |
||
|
断裂伸长率 |
-40℃ |
ASTM D-638 |
4.5 |
% |
|
|
23℃ |
ASTM D-638 |
5.0 |
% |
||
|
80℃ |
ASTM D-638 |
6.0 |
% |
||
|
弯曲强度 |
-40℃ |
ASTM D-790 |
305 |
MPa |
|
|
23℃ |
ASTM D-790 |
260 |
MPa |
||
|
80℃ |
ASTM D-790 |
145 |
MPa |
||
|
弯曲模量 |
-40℃ |
ASTM D-790 |
11.0 |
Gpa |
|
|
23℃ |
ASTM D-790 |
8.8 |
Gpa |
||
|
80℃ |
ASTM D-790 |
4.4 |
Gpa |
||
|
压缩强度 |
-40℃ |
ASTM D-695 |
250 |
MPa |
|
|
23℃ |
ASTM D-695 |
180 |
MPa |
||
|
80℃ |
ASTM D-695 |
95 |
MPa |
||
|
肖氏强度 |
23℃ |
ASTM D-732 |
85 |
MPa |
|
|
冲击强度 |
-40℃ |
ASTM D-256 |
85 |
J/M |
|
|
23℃ |
ASTM D-256 |
125 |
J/M |
||
|
-40℃ |
ASTM D-256 |
70 |
KJ/m2 |
||
|
23℃ |
ASTM D-256 |
80 |
KJ/m2 |
||
|
电气性能 |
体积电阻率 |
|
ASTM D-257 |
1013 |
Ω.m |
|
热性能 |
熔点 |
|
|
225 |
℃ |
|
比热 |
|
|
1.6 |
J/g℃ |
|
|
线膨胀系数 |
|
|
0.38 |
W/M.℃ |
|
|
热变形温度 |
0.46Mpa |
D-648 |
224 |
℃ |
|
|
1.86MPa |
D-648 |
215 |
℃ |
||
|
阻燃性 |
|
UL94 |
HB |
|
|
『PA6(聚已内酰胺#尼龙6)』
美国杜邦：73M30 NC010
泰国宇部 (日本宇部)：1013B、1030B、1015B、1022B
日本帝斯曼(日本三菱)：1010C2、1015G30
德国巴斯夫：B3EG6、B3WG6、B3EG3、B3S、B3K、B3WG10、B3EG5、B3ZG3、B3GM35
台湾集盛：TP-4208、BF1206
余姚金树业：GF630
南京利华：B709
日本东丽：CM1014-V0、CM1021、CM1017、CM1016G-30
荷兰D***：F223-D、K225-KS、K224-G6
巴陵石化：BL2280-Z
巴陵化纤：YH800
朗盛：BKV30H2.0、B30S
石家庄庄缘:1013B
南京德尔隆：B706、B9000
另有其它型号请来电咨询！