PMMA(聚甲基***甲酯#有机玻璃|压克力)/IG840/LG化学
用途： 其它
重要参数： 熔体流动速率:5.8 g/10min 密度:1.18 g/cm3 吸水率:0.3 % 成型收缩率:0.4 % 缺口冲击强度:1.6 拉伸强度:69 MPa 弯曲强度:119 MPa 弯曲模量:3234 MPa 硬度:93 维卡软化点:100 ℃ 热变形温度:96 ℃ 透光率:93 %
生产厂商：韩国LG化学
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24h | ASTM D-570 | 0.3 | % |
| 物理性能 | 反射指数 | --- | ASTM D-542 | 1.49 | --- |
| 比重 | --- | ASTM D-792 | 1.18 | --- | |
| 透明性 | 3.2mm | ASTM D-1003 | 93 | % | |
| 机械性能 | 流动指数 | 230°C,3.8kg | ASTM D-1238 | 5.8 | g/10min |
| 模缩系数 | --- | ASTM D995-51 | 0.2-0.6 | % | |
| 拉力 | --- | ASTM D-638 | 710 | Kg/cm2 | |
| 延伸率 | --- | ASTM D-638 | 3.5 | % | |
| 弯曲强度 | --- | ASTM D-790 | 1,220 | Kg/cm2 | |
| 弯曲模数 | --- | ASTM D-790 | 33,000 | Kg/cm2 | |
| 冲击强度 | Izod Notched | ASTM D-256 | 1.6 | kg・cm/cm2 | |
| 洛氏硬度 | M-Scale | ASTM D-785 | 93 | --- | |
| 电气性能 | ***积系数 | --- | ASTM D-257 | >1515 | Ω.m |
| 介电强度 | 4KV/S | ASTM D-149 | 20 | KV/mm | |
| 介电定数 | 60Hz | ASTM D-150 | 4 | --- | |
| 功率系数 | 60Hz | ASTM D-150 | 0.05 | --- | |
| 热 性 能 | 燃烧率 | 1/8",1/16" | UL94 | HB | --- |
| 维卡软化点 | 1kg | ASTM D-1525 | 100 | °C | |
| 比热 | --- | --- | 0.35 | cal/g/°C | |
| 绵性膨胀系数 | --- | ASTM D-696 | 6×10-5 | cm/cm/°C | |
| 热传导 | --- | ASTM D-177 | 5×10-4 | cal/seccm・°C/cm | |
| 热变形温度 | 18.56kg | ASTM D-648 | 96 | °C | |