101L BKB009
|
性能项目 |
测试条件 |
测试方法 |
数值/描述 |
单位 |
|
|
机械性能 |
拉伸强度(引张强度) |
|
ASTM D638/ISO 527 |
88 |
kg/cm2(MPa)[Lb/in2] |
|
断裂伸长率 |
|
ASTM D638/ISO 527 |
16 |
% |
|
|
拉伸模量 |
|
ASTM D638/ISO 527 |
3050 |
kg/cm2(MPa)[Lb/in2] |
|
|
拉伸屈服伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
|
拉伸断裂伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
|
弯曲模量(弯曲弹性率) |
|
ASTM D790/ISO 178 |
2800 |
kg·cm/cm(J/M)ft·lb/in |
|
|
弯曲强度 |
|
ASTM D790/ISO 178 |
|
kg·cm/cm(J/M)ft·lb/in |
|
|
洛氏硬度 |
|
ASTM D785 |
|
|
|
|
IZOD 缺口冲击强度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
|
1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
Charpy冲击强度 |
23℃ （缺口） |
ASTM D256/ISO 179 |
4 |
kg·cm/cm(J/M)ft·lb/in |
|
|
-30℃（缺口） |
ASTM D256/ISO 179 |
3.7 |
kg·cm/cm(J/M)ft·lb/in |
||
|
23℃（无缺口） |
ASTM D256/ISO 179 |
203 |
kg·cm/cm(J/M)ft·lb/in |
||
|
-30℃（无缺口） |
ASTM D256/ISO 179 |
134 |
kg·cm/cm(J/M)ft·lb/in |
||
|
物性性能 |
比重（密度） |
|
ASTM D792/ISO 1183 |
1.14 |
|
|
成型收缩率 |
|
ASTM D955 |
|
% |
|
|
熔融指数（流动系数） |
200℃/5kg |
ASTM D1238/ISO 1133 |
|
g/10min |
|
|
220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
||
|
吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
|
% |
|
|
热性能 |
热变形温度 |
退火 |
ASTM D648/ISO 75 |
200 |
℃（℉） |
|
未退火 |
ASTM D648/ISO 75 |
70 |
℃（℉） |
||
|
维卡软化点 |
|
ASTM D1525/ISO R306 |
|
℃（℉） |
|
|
熔点 |
|
- |
262 |
℃（℉） |
|
|
燃烧性（率） |
|
UL94 |
V-2 |
|
|
|
线性膨胀系数 |
|
ASTM D696/ISO 11359 |
|
mm/mm.℃ |
|
|
电气性能 |
介电常数 |
100HZ |
ASTM D150/IEC 60250 |
|
|
|
1MHZ |
ASTM D150/IEC 60250 |
|
|
||
|
体积电阻率 |
|
ASTM D257/IEC 60093 |
|
Ω.cm |
|
|
表面电阻率 |
|
ASTM D257/IEC 60093 |
|
Ω |
|
|
耐电弧性 |
|
ASTM D495/IEC 60112 |
|
|
|
|
加工条件 |
干燥条件 |
|
|
|
|
|
加工温度 |
射嘴 |
|
|
℃ |
|
|
料筒前段 |
|
|
℃ |
||
|
料筒中段 |
|
|
℃ |
||
|
料筒后段 |
|
|
℃ |
||
|
熔体温度 |
|
|
|
℃ |
|
|
模具温度 |
|
|
|
℃ |
|
|
压力 |
注塑压力 |
|
|
Mpa |
|
|
保压压力 |
|
|
Mpa |
||
|
背压 |
|
|
Mpa |
||
|
螺杆转速 |
|
|
|
rpm |
|
|
其他 |
备注 |
|
|||
|
颜色 |
|
||||
|
特性 |
PA66,***成型 |
||||
|
用途 |
|
||||