原包朗盛PBT Pocan B4225
金先生159-1681-6001
*** 1362174071
|
|
||||||||||||
| 密度 | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| 吸水率 | 0.30 % | 0.30 % | Test Sim. to ISO 62 |
| 平衡吸湿 | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| 粘度测试 | 97 cm³/g | 97 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| 线性成型收缩率,Flow | 0.0049 cm/cm | 0.0049 in/in | ISO 294-4, 2577 |
| 线性成型收缩率，横向 | 0.0018 cm/cm | 0.0018 in/in | ISO 294-4, 2577 |
| 简支梁无缺口冲击强度 | 4.00 J/cm²
@Temperature -30.0 °C
|
19.0 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU |
| 4.00 J/cm²
@Temperature 23.0 °C
|
19.0 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU | |
| 简支梁缺口冲击强度 | <= 1.00 J/cm²
@Temperature -30.0 °C
|
<= 4.76 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| <= 1.00 J/cm²
@Temperature 23.0 °C
|
<= 4.76 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA | |
| 冲击 | 628 | 628 | Puncture maximum force (N); ISO 6603-2 |
| 多轴向仪器化冲击能量 | 1.80 J | 1.33 ft-lb | ISO 6603-2 |
| 拉伸蠕变模量(1 hr) | 7300 MPa | 1.06e+6 psi | ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 6900 MPa | 1.00e+6 psi | ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| 可燃性(UL94) | V-2
@Thickness 0.800 mm
|
V-2
@Thickness 0.0315 in
|
IEC 60695-11-10 |
| V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
IEC 60695-11-10 | |
| 5VA
@Thickness 3.50 mm
|
5VA
@Thickness 0.138 in
|
IEC 60695-11-20 |
PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，***适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.
原包朗盛PBT Pocan B4225