1.20CrMnMo渗碳钢的特性:80mm厚***定扎***20CrMnMo钢板
20CrMnMo钢是一种高强度的***渗碳钢,归于Cr-Mn-Mo系列合金结构钢,20CrMnMo渗碳钢强度高于15CrMnMo,塑性及耐性稍低,20CrMnMo钢淬火回火后有杰出的归纳力学功能和低温冲击韧度,淬透性及力学功能比20CrMnTi钢较高,与12CrNi3A钢恰当,比20CrNi3A钢稍低;20CrMnMo钢渗碳淬火后具有较高的抗弯强度和耐磨功能,渗碳后其剩余奥氏体含量较高,不宜直接淬火;20CrMnMo钢的功能与日本合金结构钢SCM421附近,20CrMnMo钢用于制作要求外表硬度高、耐磨功能好的重要渗碳件,如齿轮、凸轮轴连杆、销等;20CrMnMo钢热加工功能杰出,正火后切削加工功能好,切削加工性优于12CrNi3A钢和20CrNi3A钢,但磨削时易发生裂纹,焊接功能较差,20CrMnMo钢合适于电阻焊接,焊前要恰当预热,焊后应及时回火。
20CrMnMo steel is a kind of high-strength high-grade carburizing steel, belonging to Cr Mn Mo series alloy structural steel. 20CrMnMo carburizing steel has higher strength than 15crmnmo, lower plasticity and toughness. After quenching and tempering, 20CrMnMo steel has good comprehensive mechanical properties and low-temperature impact toughness, higher hardenability and mechanical energy than 20CrMnTi steel, equivalent to 12CrNi3A steel, slightly lower than 20crni3a steel; 20CrMnMo steel has carburizing and quenching After carburizing, it has high bending strength and wear resistance, and the content of retained austenite is high, so it is not suitable to be quenched directly; the performance of 20CrMnMo steel is similar to that of scm421 alloy structural steel. Henan Changsheng iron and Steel Co., Ltd. recommends 20CrMnMo steel to be used for manufacturing important Carburized parts with high surface hardness and good wear resistance, such as gears, camshaft connecting rods, pins, etc.; 20CrMnMo steel hot working After normalizing, the machinability is better than 12CrNi3A steel and 20crni3a steel, but it is easy to produce cracks during grinding, and the welding performance is poor. 20CrMnMo steel is suitable for resistance welding. Before welding, it should be preheated properly and tempered in time.
2.20CrMnMo渗碳钢的化学成分:
碳 C :0.17-0.23%
硅 Si:0.17~1.37%
锰 Mn:0.90~1.20%
硫 S :答应剩余含量≤0.035%
磷 P :答应剩余含量≤0.035%
铬 Cr:1.10~1.40%
镍 Ni:答应剩余含量≤0.030%
铜 Cu:答应剩余含量≤0.030%
钼 Mo:0.20~0.30%
3.20CrMnMo渗碳钢的力学功能:
抗拉强度σb (MPa):≥1175(120)
屈从强度 σs (MPa):≥885(90)
伸长率 δ5 (%):≥10
断面缩短率ψ (%):≥45
冲击功 Akv (J):≥55
冲击耐性值 αkv (J/cm2):≥69(7)
硬度 :≤217HB
试样尺度:试样毛坯尺度为15mm

4.20CrMnMo渗碳钢的热处理标准及金相安排:
热处理标准:
(1)淬火:加热温度850&plu***n;15℃,油冷。
(2)回火:加温温度200&plu***n;20℃,水冷或空冷。
金相安排:回火马氏体。
5.20CrMnMo渗碳钢的交货状况:
20CrMnMo渗碳钢一般是以热处理(正火、退火或高温回火)或不热处理状况交货,交货状况应在合同中注明。
6.20CrMnMo渗碳钢的用处:
20CrMnMo渗碳钢合适用于制作要求外表硬度高、耐磨性好的重要渗碳零件,如齿轮、凸轮、曲轴、连杆、活塞销、球头销、石油钻机的牙轮、钻头号。
20CrMnMo carburizing steel is suitable for manufacturing important carburizing parts with high surface hardness and good wear resistance, such as gears, cams, crankshafts, connecting rods, piston pins, ball pins, drilling rigs' rollers, drills, etc.