| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D 792 |
| Additive Loading | 10 % | 10 % | Primary Additive |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0020 in/in @Thickness 0.126 in |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 128 MPa | 18500 psi | ASTM D 638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D 638 |
| Tensile Modulus | 12.8 GPa | 1850 ksi | ASTM D 638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D 790 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.20 mm |
0.600 ft-lb/in @Thickness 0.126 in |
ASTM D 256 |
| Izod Impact, Unnotched | 3.20 J/cm @Thickness 3.20 mm |
6.00 ft-lb/in @Thickness 0.126 in |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 307 - 329 °C | 585 - 625 °F | |
| Mold Temperature | 135 - 177 °C | 275 - 350 °F | |
| Drying Temperature | 149 °C @Time 21600 sec |
300 °F @Time 6.00 hour |
|
| Moisture Content | 0.040 % | 0.040 % | |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | |