| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | 10 s delay; ASTM D 2240 |
| Tensile Strength at Break | 5.17 MPa @Thickness 3.20 mm |
750 psi @Thickness 0.126 in |
Die C; 20 in/min (500 mm/min); ASTM D 412 |
| Tensile Strength, Yield | 2.90 MPa @Strain 100 %, Thickness 3.20 mm |
420 psi @Strain 100 %, Thickness 0.126 in |
Die C; 20 in/min (500 mm/min); ASTM D 412 |
| Elongation at Break | 500 % @Thickness 3.20 mm |
500 % @Thickness 0.126 in |
Die C, 20 in/min (500 mm/min); ASTM D 412 |
| Tear Strength | 27.2 kN/m | 155 pli | Die C; ASTM D 624 |
Compression Set  |
30 % @Temperature 23.0 °C, Time 79200 sec |
30 % @Temperature 73.4 °F, Time 22.0 hour |
Method B, Type 2; ASTM D 395 |
| 48 % @Temperature 70.0 °C, Time 79200 sec |
48 % @Temperature 158 °F, Time 22.0 hour |
Method B, Type 2; ASTM D 395 | |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 210 °C | 360 - 410 °F | |
| Mold Temperature | 15.6 - 65.6 °C | 60.0 - 150 °F | |
| Drying Temperature | 79.4 °C @Time 7200 sec |
175 °F @Time 2.00 hour |
|
| Moisture Content | 0.030 % | 0.030 % | |
| Dew Point | -17.8 °C | 0.000 °F | |
| Injection Pressure | 82.7 - 124 MPa | 12000 - 18000 psi | |