| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 55.0 | 55.0 | 10 s delay; ASTM D 2240 |
| Tensile Strength at Break | 5.52 MPa | 800 psi | Die C, 0.125 in (3.2mm); 20 in/min (500 mm/min); ASTM D 412 |
| Tensile Strength, Yield | 2.07 MPa | 300 psi | Die C 0.125 in (3.2 mm); 20 in/min (500 mm/min); 100%; ASTM D 412 |
| Elongation at Break | >= 500 % | >= 500 % | Break; Die C, 0.125 in (3.2mm); 20 in/min (500 mm/min); ASTM D 412 |
| Tear Strength | 30.7 kN/m | 175 pli | Die C; ASTM D 624 |
| Peel Strength | 5.43 kN/m | 31.0 pli | PC/PBT; 90 degrees, 20 in/min (500 mm/min); ISO 813 |
| 5.78 kN/m | 33.0 pli | PC/PMMA; 90 degrees, 20 in/min (500 mm/min); ISO 813 | |
Compression Set  |
19.0 % @Temperature 23.0 °C, Time 79200 sec |
19.0 % @Temperature 73.4 °F, Time 22.0 hour |
Method B; Type 2; ASTM D 395 |
| 65.0 % @Temperature 70.0 °C, Time 79200 sec |
65.0 % @Temperature 158 °F, Time 22.0 hour |
Method B; Type 2; ASTM D 395 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 193 - 238 °C | 380 - 460 °F | |
| Mold Temperature | 21.1 - 48.9 °C | 70.0 - 120 °F | |
| Drying Temperature | 76.7 °C @Time 7200 - 14400 sec |
170 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.0400 % | <= 0.0400 % | |