| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm @Thickness 3.20 mm |
0.010 - 0.020 in/in @Thickness 0.126 in |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | 10 s delay; ASTM D 2240 |
| Tensile Strength at Break | 13.8 MPa @Thickness 3.20 mm |
2000 psi @Thickness 0.126 in |
Break, Die C, 20 in/min (500 mm/min); ASTM D 412 |
Tensile Strength, Yield  |
2.28 MPa @Strain 50.0 % |
330 psi @Strain 50.0 % |
Die C 0.125 in (3.2 mm); 20 in/min (500 mm/min); ASTM D 412 |
| 2.90 MPa @Strain 100 % |
420 psi @Strain 100 % |
Die C 0.125 in (3.2 mm); 20 in/min (500 mm/min); ASTM D 412 | |
| 5.38 MPa @Strain 300 % |
780 psi @Strain 300 % |
Die C 0.125 in (3.2 mm); 20 in/min (500 mm/min); ASTM D 412 | |
| Elongation at Break | 500 % @Thickness 3.20 mm |
500 % @Thickness 0.126 in |
Die C, 20 in/min (500 mm/min); ASTM D 412 |
| Tear Strength | 46.5 kN/m | 265 pli | Die C; ASTM D 624 |
| Compression Set |
25 % @Temperature 23.0 °C, Time 79200 sec |
25 % @Temperature 73.4 °F, Time 22.0 hour |
Method B; Type 2; ASTM D 395 |
| 80 % @Temperature 70.0 °C, Time 79200 sec |
80 % @Temperature 158 °F, Time 22.0 hour |
Method B; Type 2; ASTM D 395 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 193 - 238 °C | 380 - 460 °F | |
| Mold Temperature | 21.1 - 48.9 °C | 70.0 - 120 °F | |
| Drying Temperature | 82.2 °C @Time 7200 - 14400 sec |
180 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.030 % | <= 0.030 % | |