PCS4001导电银浆苏州普强导电涂料有限公司开发生产的一种慢干型热固化银浆；具有良好的丝印适性和低阻值性。
用途
广泛应用于薄膜开关、电脑键盘、柔性线路板等领域。
特点
1.较强的导电性
2.极佳的附着力
3.优秀的挠曲性
4.良好的印刷性
技术数据
|
产品
性能指标 |
PCS4001 |
|
填料 |
银粉 |
|
固体含量（Wt%） |
60±2% |
|
方阻(Ω/□) |
12Ω/□ |
|
粘度
（Viscometer14#，20rpm,25℃ ） |
25~35Pa•S |
|
理论覆盖面积（25um） |
5-7 m2／KG |
|
挠曲性（导线宽1mm，2公斤力×180°外折×1分钟×5次以上) |
△R <2Ω |
|
附着力
（3M600胶带×1分钟，垂直拉） |
无脱落 |
|
硬度 |
>2H |
|
固化条件 |
140℃*40Min |
|
保质期 |
密封3个月 |
方法
1. PCS4001是即用产品，无需稀释；如需稀释，应使用我司专用稀释剂DBE并搅拌均匀。
2. 银浆使用应是已回复室温。
3. 使用前请轻轻搅拌，速度不宜太快，防止渗入空气。
4. 建议使用200-300目不锈钢丝网或聚脂丝网印刷。
5. 干燥温度为140℃×30分钟。
注意事项
1.使用时应保持通风良好，以避免过量蒸汽吸入体内。
2.如接触到皮肤,应及时用清水和肥皂清洗。
3.银浆的存放应拧紧瓶盖，置于＜15℃室内阴凉处。
Conductive silver paste has halogen Series
PCS4001 conductive silver paste PuQiang (suzhou) conductive Paints Co.,LTD. Development and production of a slow-curing hot-dry silver paste; has a good screen printing and low adaptive value of.
Application
Widely used in thin film switches, computer keyboards, flexible circuit boards and other fields
Technical Data
|
Products
Property |
PCS4001 |
|
Filler |
Silver |
|
Solid Content (Wt%) |
60±2% |
|
Resistance(Ω/□) |
<12Ω/□ |
|
Viscosity（Viscometer14#，20rpm,25℃ ） |
25~35Pa•S |
|
Theoretical coverage（25um） |
5-7 m2／KG |
|
Deflection of（Wide wire1mm，2Kgf×180°Outside the fold×1Minutes×5TimesAbove) |
△R <2Ω |
|
Adhesion（3M600Tape×1Minutes，Vertical pull） |
No shedding |
|
Hardness |
>2H |
|
Curing conditions |
140℃*30Min |
|
Shelf-life |
Sealed 3 months |
Application Method
1.PCS4001 Products are used without dilution; For dilution, the Secretary should use my special diluent and mixing evenly DBE.
2.Silver has returned to use should be at room temperature.
3.Stir gently before use, speed should not be too fast, to prevent the infiltration of air.
4.Recommend the use of 200-300 head of stainless steel or polyester screen printing mesh.
5.Drying temperature of 140 ℃ × 40 minutes.
Notes
1. Use good ventilation should be maintained in order to avoid excessive steam inhaled.
2. Such as contact with the skin should be promptly cleaned with water and soap.
3. Silver storage cap should be tightened, placed <15 ℃ interior cool place.