Type              

T 46 2 (4)P C(M) 1 H5

E 71 T-1

Micro- Alloy rutile flux-cored wire with rapidly solidefying slag for C02 and Ar-Co2 mix. Excellent weld puddle manipulation, thus superior all-postion welding also at higher currents. Using temperature up to -40C. Particulary suited for MAG-orbital welding and all-position welding on ceramic backing. Low spatter loss, easy slag removal.

Shipbuilding, steel and pressure vessel c***truction, mechanical engineering and pipe work.

T 46 A Z P C(M) 1 H5

E 81 T1-G

Micro- Alloy rutile flux-cored wire with rapidly solidefying slag for C02 and Ar-Co2 mix. Excellent weld puddle manipulation, thus superior all-postion welding. Particulary suited for mechanized MAG welding and all-position welding on ceramic backing. Low spatter loss, easy slag removal.

Weathering grades of steels.

 

 

 

T 50 6 1Ni P M1 H5
T 46 4 1Ni P C1 H5

E 81 T1-Ni1

Micro- Alloy rutile flux-cored wire with rapidly solidefying slag for C02 and Ar-Co2 mix. Excellent weld puddle manipulation, thus superior all-postion welding. Using temperature up to -60C. Particularly suited for MAG orbital welding applicati*** and all-position welding on ceramic backing.  Low spatter loss, easy slag removal. CTOD-tested for offshore applicati***.

Shipbuilding, steel and pressure vessel c***truction, mechanical engineering and pipe work.

T 46 A P M1 H5

E 81T1-A1

Micro-alloy rutile flux-cored wire with rapidly solidfying slag for Ar-C02 mix.
Excellent weld puddle manipulation, thus superior all-postion welding.
Particulary suited for mechanized MAG welding and all-position welding on ceramic backing. Low spatter loss, easy slag removal.

Shipbuilding, steel and pressure vessel c***truction, mechanical engineering and pipe work.

T CrMo 1 P M 1 H5

E 81 T1-B2

Still in research

T 69 6 Mn2,5Ni P M 2 H5

E 110 T5-K4

Micro- Alloy rutile flux-cored wire with rapidly solidefying slag for C02 and Ar-Co2 mix. Excellent weld puddle manipulation, thus superior all-postion welding. Using temperature up to -60C. Particularly suited for MAG orbital welding applicati*** and all-position welding on ceramic backing.  Low spatter loss, easy slag removal. Recomended for offshore applicati*** that requires yield strenght up to 690 N/mm2.
Approved by LLoyds (4Y69) and DNV.

(The first and only seamless fluxcored rutile wire for StE 690 on the marked ! )

Type               

T 46 4 M M 1 H5

E 70 C-6M
E 71 T-1

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag. High mechanical properties are easily obtained when used in singel sided welding operati*** using a ceramic back-up. Weld X-ray quality with low spatter formation. Ideal metalurgical choice for repair welding and production as well as for use as a buffer layer.
Shipbuilding, steel and vessel contruction, pipe work

T 46 2 Mo M M 1H5

E 81 T1-A1
E 80 C - G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high temperature resistant Mo-steels up to 500C.
Weld X-ray quality with low spatter formation.
Shipbuilding, steel and vessel c***truction, mechanical engineering and pipe work

T CrMo 1 M M 1 H5

E 80 T5-B2

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high temperature resistant Mo-steels up to 550C.
Weld X-ray quality with low spatter formation.
Shipbuilding, steel and vessel c***truction, mechanical engineering and pipe work

T 50 4 Z M M 1 H5

E 81 T1-G
E 80 C-G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high temperature and compressed hydrogen resistant 2,25 Cr 1MO steels. Meets requirements of step cooling by very low weld metal contaminati***.
Pressure vessels, chemical apparatus and steam-turbine c***truction.

T 50 41NiMoMM1H5

E 91 T1-G
E 80 C-G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high temperature resistant hydrogen CrMoV-steels up to 550C. Weld X-ray quality with low spatter formation.
Foundries, production welding.

T 55 6 Z M M 1 H5

E 91 T1-G
E 80 C-G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high temperature resistant fine grain structural steels. Weld X-ray quality with low spatter formation. Uniform weld, easy slag release.
Cranes, vessels and apparatus c***truction, foundries

T 69 6 Z M M 1H5

E 111 T1-G
E 110 C-G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high temperature resistant fine grain structural steels. Weld X-ray quality with low spatter formation. Uniform weld, easy slag release.
Cranes, vessels and apparatus c***truction, foundries

T 69 4Mn2NiCrMoMM 1H5

E 111 T1 - K4

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high strength resistant and cryogenic fine grain structural steels with Rp0,2 > 690N/mm². Weld X-ray quality with low spatter formation. Stable mechanical property ＆#118alues of weld metal, also in case of high input of heat up to 18kJ/cm.
Cranes, automobile, equipment, vessels and apparatus c***truction, foundries.

T 89 4 Z M M 1 H5

E 120 T1-G
E 110 C-G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high strength temperature resistant and cryogenic fine grain structural steels with Rp0,2 > 890N/mm². Weld X-ray quality with low spatter formation. Stable mechanical property ＆#118alues of weld metal, also in case of high input of heat up to 15kJ/cm.
Cranes, automobile, equipment, vessels and apparatus c***truction, foundries.

T 89 4 Z M M 1 H5

E 120 T1-G
E 110 C-G

High-basicity flux-cored wire with slag for C02 and Ar-Co2 mix.
Extremely crack resistant weld metal conditioned by the basic slag in combination with the very low hydrogen content. Well suited for the economic joining of high strength temperature resistant fine grain structural steels with Rp0,2 > 890N/mm². Weld X-ray quality with low spatter formation. Stable mechanical property ＆#118alues of weld metal, also in case of high input of heat up to 15kJ/cm. The MEGAFIL 807 B has a heat treatable weld metal.
Cranes, automobile, equipment, vessels and apparatus c***truction, foundries.

T 46 4 M M 1 H5

E 70 C-6M
E 71 T-1

Metal powder cored wire without slag for Ar-C02 mix.
Good arc restrinking even with cold wire tip, thus beeing suitable for robot applicati***. Multi-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding.

Shipbuilding, steel and pressure vessel c***truction, mechanical engineering and pipe work.

T 46 2 Mo M M 1H5

E 81 T1-A1
E 80 C-G

Metal powder cored wire without slag for Ar-C02 mix.
Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Vessel and steel c***truction, mechanical engineering and pipe work.

T CrMo 1 M M 1 H5

---

Metal powder cored wire without slag for Ar-C02 mix.
Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Vessel and steel c***truction, mechanical engineering and pipe work.

T 50 4 Z M M 1 H5

E 81 T1-G
E 80 C-G

Metal powder cored wire without slag for Ar-C02 mix.
Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Crane, steel, vessels and apparatus c***truction.

T 50 4 1NiMo M M 1 H5

E 91 T1-G
E 80 C-G

Metal powder cored wire without slag for Ar-C02 mix.
Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Crane, steel, vessels and apparatus c***truction.

T 55 6 Z M M 1 H5

E 91 T1-G
E 80 C-G

Medium-alloy, high-strength metal powder flux-cored wire without slag for Ar-C02 mix.
Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Shipbuilding, crane, steel, vessels and apparatus c***truction.

T 69 6 Z M M 1H5

E 111 T1-G
E 110 C-G

Medium-alloy, high-strength metal powder flux-cored wire without slag for Ar-C02 mix.Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Shipbuilding, crane, steel, vessels and apparatus c***truction.

T 69 4 Mn2NiCrMo M M 1H5

E 111 T1 - K4

Metal powder flux-cored wire without slag for Ar-C02 mix.Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Crane, steel, vessels and apparatus c***truction.

T 89 4 Z M M 1 H5

E 120 T1-G
E 110 C-G

Metal powder flux-cored wire without slag for Ar-C02 mix.Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments. Weld metal is heat treatable.

Crane, steel, vessels and apparatus c***truction.

T 89 4 Z M M 1 H5

E 120 T1-G
E 110 C-G

Metal powder flux-cored wire without slag for Ar-C02 mix.Good arc restrinking even with cold wire tip, thus beeing suitable for robot lti-pass welding without in-between cleaning.
Ideal for use in the field short arc and spray arc. Excellent gap bridging for root welding. High- efficiency type for economic production environments.

Crane, steel, vessels and apparatus c***truction.