LDPE(低密度聚乙烯#高压聚乙烯)/LDF-260GG/马来西亚大藤
原料描述部分
|
规格级别 |
薄膜 |
|
该料用途 |
加工薄膜 |
|
备注说明 |
特性：良好的加工性 |
原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
|
基本性能 |
密度 |
23℃ |
ASTM D-1505 |
0.922 |
g/cm3 |
|
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
5 |
g/10min |
|
|
物理性能 |
光泽度 |
60℃ |
ASTM D-2457 |
10 |
g/µm |
|
混浊 |
|
ASTM D-1003 |
7 |
% |
|
|
机械性能 |
极限伸长率 |
MD |
ASTM D-882 |
250 |
% |
|
TD |
ASTM D-882 |
440 |
% |
||
|
1%割线模量 |
MD |
ASTM D-882 |
220 |
MPa |
|
|
TD |
ASTM D-882 |
270 |
MPa |
||
|
落镖冲击强度 |
|
ASTM D-1709 |
2.5 |
g/µm |
|
|
Elmendort断裂强度 |
MD |
ASTM D-1922 |
9.5 |
g/µm |
|
|
TD |
ASTM D-1922 |
4 |
g/µm |
||
|
断裂拉伸强度 |
MD |
ASTM D-882 |
19 |
MPa |
|
|
TD |
ASTM D-882 |
25 |
MPa |
||
|
热性能 |
维卡软化点 |
1kg |
ASTM D-1525 |
93 |
℃ |