900 物性表| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 密度 | 1.42 | ASTM D-792 |
| 物理性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 吸水量 | ASTM D-570 | ||
| (24hrs浸泡+73℉(+23℃)) | 0.25 | % | |
| (浸泡均衡点+73℉(+23℃)) | 0.90 | % | |
| (Equil.50%R.h.+73℉(+23℃)) | 0.22 | % |
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|---|---|---|
| 弯曲疲劳忍耐限度 (+23℃) | 31.7 | MPa | ASTM D-671 |
| 扩散因数 (+73℉(+23℃)10Hz) | 0.005 | ASTM D-150 | |
| 线性热膨胀系数 (+85 to +140℉) | 6.8 | 10-5in/in.℉ | ASTM D-696 |
| 弹性系数 (+73℉) | 450 | MPsi | ASTM D-638 |
| 负载下之变形 (2000psi@+122℉(14Mpa@50℃)) | 0.5 | % | ASTM D-621 |
| 弯曲降服强度 (+73℉) | 14.0 | MPsi | ASTM D-790 |
| 断裂时之拉力伸张度 (+212℉(+100℃)) | >260 | % | ASTM D-638 |
| 伸张强度 | ASTM D-638 | ||
| (-55℃) | 101 | MPa | |
| (+250℉) | 3.8 | MPsi | |
| 弯曲疲劳忍耐限度 (+73℉) | 4.6 | MPsi | ASTM D-671 |
| IZOD冲击强度 (40℃) | 53.4 | j/m | ASTM D-256 |
| 拉力冲击抵抗力 (+73℉) | 70 | ft.lb/in | ASTM D-1822 |
| 无切口冲击程度 (+73℉) | 16 | ft.lb/in | ASTM D-256 |
| 断裂时之拉力伸张度 (-68℉(-55℃)) | 10 | % | ASTM D-638 |
| 伸张强度 (+100℃) | 35.9 | MPa | ASTM D-638 |
| IZOD冲击强度 (-40℉) | 1.0 | ft.lb/in | ASTM D-256 |
| 压缩应力 (+73℉@1%ASTM D-ef.) | 5.0 | MPsi | ASTM D-695 |
| 伸张强度 (-68℉) | 14.7 | MPsi | ASTM D-638 |
| 挠曲系数 (+158℉) | 240 | MPsi | 在25℃下 |
| 无切口冲击程度 (+23℃) | 850 | j/m | ASTM D-256 |
| 伸张强度 (+212℉) | 5.2 | MPsi | ASTM D-638 |
| 压缩应力 (+73℉@10%ASTM D-ef.) | 17.6 | MPsi | ASTM D-695 |
| 挠曲系数 (+250℉) | 90 | MPsi | 在25℃下 |
| IZOD冲击强度 (+23℃) | 69.4 | j/m | ASTM D-256 |
| 伸张强度 (+158℉) | 6.9 | MPsi | ASTM D-638 |
| 弯曲降服强度 (+23℃) | 96.5 | MPa | ASTM D-790 |
| 拉力冲击抵抗力 (+23℃) | 150 | kj/m | ASTM D-1822 |
| 压缩应力 (+23℃@1%ASTM D-ef.) | 34.5 | MPa | ASTM D-695 |
| 弹性系数 (+23℃) | 3100 | MPa | ASTM D-638 |
| 伸张强度 (+23℃) | 68.9 | MPa | ASTM D-638 |
| 洛氏硬度 | ***4,R120 | ASTM D-785 | |
| 挠曲系数 | 在25℃下 |